WELD METAL ANALYSIS (RANGE) %| C | Mn | Si | S | P | Ni | Cr | Mo | V | Mn + Ni + Cr + Mo + V |
| 0.1 | 0.80 - 1.60 | 0.75 | 0.03 | 0.03 | 0.3 | 0.2 | 0.3 | 0.08 | 1.75 max |
| max | max | max | max | max | max | max | max |
| UTS (MPa) | YS (MPa) | EL (%) (L=4D) | CVN Impact Value |
| | | | Temp | Joules |
| | | | 27°C | 120 - 200 |
| 510 min | 440 min | 24 - 30 | 0°C | 100 - 180 |
| | | -20°C | 80 - 160 |
| | | -30°C | 60 - 140 |
• For radiographic quality welding of highly stressed crack sensitive Joints in steel structures, ship building, heavy duty boilers and pressure vessels, bridges, storage tanks, high pressure pipelines etc.
• Recommended for higher carbon & higher sulphur steels, which are susceptible to hydrogen induced cracking.
REDRYING TEMPERATURE : 250°C / 2hrs
DIFFUSIBLE HYDROGEN : max 4ml / 100g of deposited weld metal.
ASME IX QUALIFICATION : QW - 432 F - NO 4, QW - 442 A - NO 1
MOISTURE CONTENT IN THE FLUX COATING : 0.40% max
PACKING PARAMETERS| Size (mm) | Length (mm) | Amps | Packing / Box (kg) | Packing / Box (Pcs) |
| AC (70 OCV) / DC (+) |
| 2.5 | 350 | 60 - 85 | 2 x 6 = 12 | 150 x 4 = 600 |
| 3.15 / 3.20 | 450 | 100 - 130 | 2 x 6 = 12 | 100 x 4 = 400 |
| 4 | 450 | 130 - 180 | 2 x 6 = 12 | 65 x 4 = 260 |
| 5 | 450 | 180 - 220 | 2 x 6 = 12 | 65 x 4 = 260 |