TYPICAL CHEMICAL COMPOSITION OF ALL WELD METAL (%)
| Element | C | Mn | Si | S | P | Cr | Ni | Mo | Cu |
| Range | 0.010 | 0.5-2.5 | 1.00 | 0.030 | 0.040 | 22.0-25.0 | 12.0-14.0 | 0.75 | 0.75 |
| Typical | 0.028 | 1.40 | 0.60 | 0.010 | 0.020 | 23.5 | 12.4 | 0.020 | 0.060 |
TYPICAL MECHANICAL PROPERTIES OF ALL WELD METAL
| Property | UTS | El |
| (MPa) | (L= 4d)% | |
| Range | 520 Min | 30 Min |
| As Weld | 570 | 38 |
CURRENT & PACKING DATA: DC (+)
| Diameter (mm) | Horizontal/ Flat | Horizontal/ Flat | Vertical UP | Vertical UP | Overhead | Overhead |
| Volt, V | Current, A | Volt, V | Current, A | Volt, V | Current, A | |
| 1.20 | 24-30 | 160-260 | 20-22 | 100-160 | 22-25 | 100-160 |
| 1.60 | 24-30 | 180-300 | 20-22 | 110-200 | 22-25 | 110-200 |
PACKING
Standard size : 1.20 & 1.60mm. Quantity : Supplied approximately 12.5/15Kgs in a plastic spool. Each spool is sealed in an air tight polythene bag and then packed in a corrugated box.
SHIELD GAS
Carbon Dioxide CO2 (100%) at flow rate 12-15 litres per minute.
WELDING POSITIONS:
H, F, VU, OH